Original Title: Performance and Application of TA10 Titanium Rod One Pure titanium bar and titanium alloy bar are new structural materials. Titanium has the characteristics of high melting point, low specific gravity, high specific strength, good toughness, fatigue resistance, acid and alkali corrosion resistance, low thermal conductivity, good high and low temperature tolerance, and low stress under rapid cooling and heating conditions. It has been used in high-tech fields such as aviation and aerospace, and has been continuously promoted to chemical, petroleum, electric power, seawater desalination,titanium tubing price, construction, daily necessities and other industries. Two Commonly used grade of titanium rod GB grades: TA1, TA2, TA3, TA7,titanium bar gr7, TA9, TA10, TA15, TA18, TC4, TC4ELI, TC6, TC9, TC10, titanium round bar ,titanium exhaust tubing, TC11 American standard: GR1, GR2, GR3, GR5, GR7, GR12 Three Titanium rod manufacturing process: Hot forging-hot rolling-annealing and straightening-turning (grinding)-polishing-flat head-inspection-packaging Four Common standards for titanium rods: GB: GB/2965-2007, GB/T13810 ASTM B348, ASTM F136, ASTM F67, AMS4928 Five Titanium rod specification: (diameter/length/mm): 6mm-250mmL Six Supply status of titanium rod: hot working status and annealing status Seven Reference Standards 1. GB 228 Metal Tensile Test Method 2. Titanium and Titanium Alloy Designation and Chemical Composition (GB/T 3620.1) 3. GB/T3620.2 Titanium and Titanium Alloy Wrought Products Chemical Composition and Allowable Deviation of Composition 4. GB 4698 Methods for Chemical Analysis of Titanium Sponge, Titanium and Titanium Alloys Expand the full text Eight Technical requirements for titanium rods 1. The chemical composition of titanium and titanium alloy bars shall conform to the provisions of GB/T 3620.1. When repeated inspection is required, the allowable deviation of chemical composition shall conform to the provisions of GB/T 3620.2. TA10（Ti-0.3Mo-0.8Ni） 2. The diameter or side length of hot-worked bars and their allowable deviations shall comply with the corresponding provisions. 3. After hot processing, the bars shall be turned (ground) and cold rolled, and the allowable diameter deviation of cold-drawn bars shall conform to the industrial regulations. 4. After hot processing, the out-of-roundness of the bar after turning (grinding) shall not be greater than half of its dimensional tolerance. Nine Purpose: Aerospace, aviation, navigation, ship, seawater desalination, petroleum, chemical industry, mechanical equipment, nuclear power equipment, electric power equipment, automobile and motorcycle parts, sports and leisure, medical parts, steel and metallurgy, high-tech fields. The nominal composition of TA10 titanium bar (Ti-Mo-Ni alloy) is Ti-0.3Mo-0.8Ni, which is a kind of Ti-12 alloy developed by the United States in the mid-1970s. It is a kind of titanium alloy with crevice corrosion resistance. The tensile strength of TA10 titanium molybdenum-nickel bar is higher than that of pure titanium TA2 and lower than that of TC4. Baoji Fanruida Titanium Industry Co.,titanium sheet grade 5, Ltd. has the same processing technology as pure titanium. The tensile strength of the alloy at 300 deg C is twice as high as that of pure titanium, the corrosion resistance to reducing media is obviously improved, and crevice corrosion does not occur in chloride at 150-200 deg C. Return to Sohu to see more Responsible Editor:. yunchtitanium.com